Customized ASTM DIN JIS EN Stainless Steel Coils With 2B BA NO.1HL 8K Surface

Material

201/202/301/304/304L/316/316L/410/420

Technique

Cold Rolled, Cold Drawn, Hot Rolled

Standard

ASTM,AISI,GB,DIN

Thickness

0.15mm-12mm or as your requirement

Width

150mm-2500mm or as your requirement

Length

Diameter as your requirement

Surface Treatment

No.1,2B,No.4,BA,2B,hairline,8k or as your needs

Packing

1. Export sea worthy package + water proof paper + wooden pallet 2. Max Loading 26mt for each 20Gp container 3. Safe loading and fixing Professional Teams 4. Professional shipping line

Delivery

Within 30 days after your 30% deposit

Application

Stainless Steel Sheets are widely used in below fields:

1: Construction field, shipping building industry

2: Petroleum and Chemical Industries

3: Food and Mechanical Industries

Quality control

Mill Test Certificate is supplied with shipment

Export

USA ,Southeast Asia, Mid East, Africa, Eastern Asia, Western Europe and So on.

Surface Finished

Characteristics

Application

BA

Bright heat treatment after cold rolling.

Ktchen utenstil, Kitchen ware, Architectural purpose.

2B

Finished by heat treatment, pickling after cold rolling, followed by skin pass line to more brighter and smooth surface.

General application medical instruments, Tableware.

NO.1

Finished by hot-rolling, annealing and pickling, characterized by white pickled surface.

Chemical industry equipment, Industrial tanks.

8K(mirror)

A mirror-like reflective surface by polishing with finer abrasives over 800 mesh.

Refletor, Mirror, Interior- Exterior decoration for building.

Hair Line

Finished by continuous linear polishing.

Architecture industries, Escalators, Kitchen ware, Vehicles.

Grade.

C %

Mn %

P %

S %

Si %

Cr %

Ni %

201

≤ 0.15

5.5-7.5

≤ 0.050

≤ 0.03

≤ 1.00

16.0-18.0

3.5-5.5

202

≤ 0.15

7.5-10

≤ 0.060

≤ 0.03

≤ 1.00

17.0-19.0

4.0-6.0

301

≤ 0.15

≤ 2

≤ 0.045

≤ 0.03

≤ 1.00

16.5-18.0

6.0-8.0

302

≤ 0.15

≤ 2

≤ 0.045

≤ 0.03

≤ 1.00

17.0-19.0

8.0-10.0

304

≤ 0.08

≤ 2

≤ 0.045

≤ 0.03

≤ 1.00

18.0-20.0

8.0-10.5

304L

≤ 0.03

≤ 2

≤ 0.045

≤ 0.03

≤ 1.00

18.0-20.0

8.0-12.0

316

≤ 0.08

≤ 2

≤ 0.045

≤ 0.03

≤ 1.00

16.0-18.0

10.0-14.0

316L

≤ 0.03

≤ 2

≤ 0.045

≤ 0.03

≤ 1.00

16.0-18.0

10.0-14.0

321

≤ 0.08

≤ 2

≤ 0.045

≤ 0.03

≤ 1.00

17.0-19.0

9.0-12.0

410

≤ 0.15

≤ 1.00

≤ 0.040

≤ 0.03

≤ 1.00

11.5-13.5

430

≤ 0.12

≤ 1.00

≤ 0.040

≤ 0.03

≤ 1.00

16.0-18.0

Grade.

Y.S N/mm2

T.S.

N/mm2

.

ELOG

%

hardness

HB

HRB

HV

301

≥ 205

≥ 520

≥ 40

≤ 207

≤ 95

≤ 218

304

≥ 205

≥ 520

≥ 40

≤ 187

≤ 90

≤ 200

304L

≥ 175

≥ 480

≥ 40

≤ 187

≤ 90

≤ 200

316

≥ 205

≥ 520

≥ 40

≤ 187

≤ 90

≤ 200

316L

≥ 175

≥ 480

≥ 40

≤ 187

≤ 90

≤ 200

321

≥ 205

≥ 520

≥ 40

≤ 187

≤ 90

≤ 200

410

≥ 205

≥ 440

≥ 20

≤ 201

≤ 93

≤ 210

430

≥ 205

≥ 450

≥ 22

≤ 183

≤ 88

≤ 200

Section 11

No.1 Finish → Hot-rolled,annealed and descaled.

No.2D Finish →

Cold-rolled,dull finish

No.2B Finish → Cold-rolled,bright finish

Bright Annealed Finish →

A bright cold-rolled finish retained by final annealing in a controlled

atmosphere furnace

No.3 Finish → Intermediate polished finish,one

or both sides

No.4 Finish → General purpose polished finish,one or both sides

No.6 Finish → Dull satin finish,Tampico brushed,one or both sides

No.7 Finish → High luster finish

No.8 Finish → Cold-worked to obtain specified properties.

Section 12

No.1 Finish → Cold-rolled to specified thickness,annealed and descaled

No.2D Finish → Same as No.1 finish,followed by a final light cold-roll pass,generally on

highly polished rolls

Bright Annealed Finish →

A bright cold-rolled finish retained by final annealing in a controlled

atmosphere furnace

TR Finish → Cold-work to obtain specified properties

Polished Finish → Stainless steel strip is also available in polished finishes such as

No.3 and No.4,which are explained in Note4.

Section 13

Hot-rolled or Cold-rolled,and Annealed or Heat treated → Scale not removed,an

intermediate

finish,Use of plates in this condition is generally confined to heat-resisting applications.

Scale impairs corrosion resistance.

Hot-rolled or Cold-rolled,and Annealed or Heat treated,and Blast cleaned or Pickled

→ Condition

and finish commonly preferred for corrosion-resisting and most heat-resisting applications,

essentially a No.1 Finish.

Hot-rolled or Cold-rolled,and Annealed or Heat treated,and surface cleaned and polishe

→ Polish finish is generally

No.4 Finish.

Hot-rolled or Cold-rolled,and Annealed or Heat treated,and Descaled; and Cold-rolled,

and Annealed Or Heat treated,and Descaled,and Optionally temper passed

→ Smooth finish with

greater freedom from surface imperfections than in 13.1.4

Section 14

No.1 Edge → A rolled edge,either round or square as specified

No.3 Edge → An edge produced by slitting.

No.5 Edge→ An approximately square edge produced by rolling or filing after slitting